Zinc immersion is conducted in a solution with immersion time for 1～2min at the operating temperature of 65℃.2.
浸锌温度为65℃,时间1～2min。
参考来源 - 镁合金表面电沉积镍的研究·2,447,543篇论文数据，部分数据来源于NoteExpress
It was found that the whiskers are formed between the grains in early stages of zinc immersion.
浸锌初期发现锌晶粒之间有晶须生成。
The temperature is too high, serious loss of zinc pot, and then affect the onset of many zinc, zinc immersion coating quality, zinc consumption, or even plating.
温度过高，锌锅铁损严峻，发作很多锌渣，然后影响浸锌层质量，锌耗大，甚至无法施镀。